| Technical Parameter |
| Steel Material | DIN 41CrA1Mo7 / AST M4140 / GB38CrMoAlA |
| Deepness of Nitriding Layer | 0.7 mm -0.9 mm |
| Hardness of Nitriding | HV900 - HV1,000 |
| Nitriding Brittleness | ≤Grade 1 |
| Chromate plating | Thickness 0.05 mm - 0.10 mm, hardnessHV950 |
| Special treatment | Carbide coating on screw flight and bimetallicbarrel |
| Screw straight tolerance | 0.015 mm/m |
| Surface roughness | Ra0.4μm |
| Technical Parameter | |
| Base Material | 1)38CrMoAlA(JIS SACM645);2)Cr12MOV(JISSKD-11) ; 3)4Cr5MoSiV1(JIS SKD-61) ;4)42CrMo(AISI4140) |
| Bimetallic Alloy Materials | 1)Fe-based alloy2)Ni-based alloy/Deloroalloy 3)Co-based alloy4)NiCo-based alloy 5)Tungsten carbide/Wolframcarbide |
| Double-alloylevel | Level A - containing Tungsten of40% Level B - containing tungsten of 25% Level C - containing tungsten of15% |
| Surface Treatment | Heat Treatment High FrequencyTreatment Nitriding treatment(120Hours): Depth of Nitrided Layer: 0.5-0.8mm Hardness of Nitrided Layer: 900-1020Hv(HRC56°-65°) HardChrome Plating treatment: Thickness of Hard Chrome Plating Layer:0.05-0.10mm Hardness ofHard Chrome Plating Layer: ≥950HV Nickel alloyplating.treatment: Bimetallic Barrel/Cylinder: Centrifugal Casting(Inlay Alloy) BimetallicScrew: Plasma Alloy Coating Spraying Depth of Bimetallic Layer: >2mm Hardness of Bimetallic Layer: HRC55°-72° Spraying corrosion wear-resisting dual metallayers |
| Basic information | Roughness of thesurface:Ra0.4um Linearity of the screw: ≤0.015mm Linear axis limit:≤0.02mm Hardness afterHardening & Tempering: HB240-280 Fragility ofNitration:≤Twoclass |
| Material Application | 1)GeneralPlastics 2)ABS,PA,PC,PE,PET,PP,PS,EVA,PU,PVC,U-PVC,etc 3)PA + GF(GlassFiber) 4)Flame-resistant Reinforced Plastics 5)Modified EngineeringPlastics 6)All kinds of Mixed Recycled Material(in Scrap or Granule), PVC +30% CaCo3, etc |